Product Details Tyfo® 111
Low Viscosity Injection Epoxy
DESCRIPTION
Tyfo® 111 Low Viscosity Injection Epoxy is a two-component, very low viscosity, high modulus
epoxy adhesive.
USE
Recommended for the repair of cracks in concrete with automatic meter, mix and dispense
pressure injection equipment.
ADVANTAGES
• Good high temperature properties
• Low Viscosity
• Resistance to creep and stress relaxation
• Excellent adhesion under adverse
application conditions (cold, wet concrete)
| Property | ASTM Method | Typical Test Value* |
|---|---|---|
| Curing Schedule, 7 days at 73° F (23° C) +/-4° F (-20° C). Test temperature, 73° F (23° C) +/-4° F (-20° C), unless otherwise specified. |
||
| Density (Pound/Gallon) |
D-1475 |
Part A = 9.4 (4.3kg) Part B = 8.1 (3.7kg) Mixed = 9.0 (4.1kg) |
| Viscosity, cps | D-2393 |
Part A 300 Part B 100 Mixed 200 |
| Viscosity @ 40° F (4° C), cps |
D-2393 |
Part A 750 Part B 425 Mixed 1,450 |
Gel Time, 5 minutes |
D-2471 |
21 |
Tensile Strength, psi |
D-638 |
9,000 (62.1 MPa) |
| Elongation at Break, Percent | D-695 |
2.0% |
| Compressive Yield Strength, psi | D-695 |
16,000 (110.3 MPa) |
| Compressive Modulus, psi |
D-645 |
410,000 (2.8 GPa) |
Heat Deflection |
D-648 |
140° F (60° C) |
| Wet Slant Shear Strength1 |
AASHTO T-237 |
Cement Mortar Failure2 |