Product Details Tyfo® WEB Composite
using Tyfo® S Epoxy
DESCRIPTION
The Tyfo® WEB Composite is an ICC-ES ESR-2103 listed product comprised of Tyfo® S Epoxy
and Tyfo® WEB reinforcing fabric. Tyfo® WEB is a custom 0o/90 degree bi-directional weave glass
fabric used in the Tyfo® Fibrwrap System. The glass material is orientated in both the 0 and 90
degree direction in optimum configuration. The Tyfo® S Epoxy is a two-component epoxy matrix
material.
USE
Tyfo® WEB Fabric is combined with Tyfo® epoxy material for lightweight reinforcement for
masonry, as a reinforced coating, and finish fabric application for bridges, buildings, and other
structures.
ADVANTAGES
• ICC-ES ESR-2103 listed product
• Good high & low temperature properties
• Long working time
• High elongation
• Ambient cure
• 100% solvent-free
• Rolls can be cut to desired widths prior to shipping
| Property | ASTM Method | Typical Test Value | Design Value* |
|---|---|---|---|
Ultimate tensile strength in |
D-3039
|
44,800 psi (309 MPa) (0.45 kip/in. width) |
35,840 psi (247 MPa) (0.36 kip/in. width) |
Elongation at break |
D-3039 |
1.6% |
1.30% |
Tensile Modulus, psi |
D-3039 |
2.8 x 106 psi (19.3 GPa) |
2.24 x 106 psi (15.4 GPa) |
| Ultimate tensile strength 90 degrees to primary fiber, psi |
D-3039 |
44,800 psi (309 MPa) (0.45 kip/in. width) |
35,840 psi (247 MPa) (0.36 kip/in. width) |
Laminate Thickness |
0.01 in. (0.25 mm) |
0.01 in. (0.25 mm) |
* Design and specification values will vary based on individual project requirements and applicable safety factors. Contact Fyfe Co. LLC engineers to determine appropriate specification values.