Product Details Tyfo® SCH-41S-1 Composite
using Tyfo® S Epoxy
DESCRIPTION
The Tyfo® SCH-41S-1 Composite is comprised of Tyfo® S Epoxy and Tyfo® SCH-41S-1
reinforcing fabric. Tyfo® SCH-41S-1 is a custom weave, uni-directional carbon fabric with glass
cross fibers. The carbon fibers are orientated in the 0o direction with glass fibers at 90o. The
Tyfo® S Epoxy is a two-component epoxy matrix.
USE
Tyfo® SCH-41S-1 Fabric is combined with Tyfo® Epoxy to add strength to bridges, buildings, and
other structures.
ADVANTAGES
• ICC-ES ESR-2103 listed product
• Good high & low temperature properties
• Long working time
• High elongation
• Ambient cure
• 100% solvent-free
• Rolls can be cut to desired widths prior to shipping
| Property | ASTM Method | Typical Test Value | Design Value* |
|---|---|---|---|
Ultimate tensile strength in |
D-3039
|
127,000 psi (876 MPa) (5.1 kip/in. width) |
107,950 psi (745 MPa) (4.3 kip/in. width) |
Elongation at break |
D-3039 |
1.2% |
1.0% |
Tensile Modulus, psi |
D-3039 |
10.5 x 106 psi (72.4 GPa) |
8.9 x 106 psi (61.5 GPa) |
| Ultimate tensile strength 90 degrees to primary fiber, psi |
D-3039 |
2,882 psi (19.9 MPa) |
2,000 psi (13.8 MPa) |
Laminate Thickness |
0.04 in. (1.0mm) |
0.04 in. (1.0mm) |
* Design and specification values will vary based on individual project requirements and applicable safety factors. Contact Fyfe Co. LLC engineers to determine appropriate specification values.