Product Details Tyfo® SEH-51A Composite
using Tyfo® S Epoxy
DESCRIPTION
The Tyfo® SEH-51A Composite is an ICC-ES ESR-2103 listed material comprised of Tyfo® S
Epoxy and Tyfo® SEH-51A reinforcing fabric. Tyfo® SEH-51A is a custom weave, uni-directional
glass fabric used in the Tyfo® Fibrwrap System. The glass material is orientated in the 0 degree
direction with additional yellow glass cross fibers at 90 degrees. The Tyfo® S Epoxy is a two-
component epoxy matrix material.
USE
Tyfo® SEH-51A Fabric is combined with Tyfo® Epoxy to add strength to bridges, buildings, and
other structures.
ADVANTAGES
• ICC-ES ESR-2103 listed product
• Component of UL listed, fire-rated assembly
• NSF/ANSI Standard 61 listed product for drinking water systems
• Good high & low temperature properties
• Long working time
• High elongation
• Ambient cure
• 100% solvent-free
• Rolls can be cut to desired widths prior to shipping
| Property | ASTM Method | Typical Test Value | Design Value* |
|---|---|---|---|
Ultimate tensile strength in
primary fiber direction, psi |
D-3039
|
83,400 psi (575 MPa) (4.17 kip/in. width) |
66,720 psi (460 MPa) (3.3 kip/in. width) |
Elongation at break |
D-3039 |
2.2% |
1.76% |
| Tensile Modulus, psi | D-3039 |
3.79 x 106 psi (26.1 GPa) |
3.03 x 106 psi (20.9 GPa) |
Ultimate tensile strength 90
degrees to primary fiber, psi |
D-3039 |
3,750 psi (25.8 MPa) |
3,000 psi (20.7 MPa) |
Laminate Thickness |
0.05 in. (1.3mm) |
0.05 in. (1.3mm) |
* Design and specification values will vary based on individual project requirements and applicable safety factors. Contact Fyfe Co. LLC engineers to determine appropriate specification values.